Ohun elo idabobo fun 10kV ati ni isalẹ Awọn okun Peroxide XLPE eyiti o ṣakiyesi resini LDPE to ti ni ilọsiwaju bi ohun elo aise akọkọ, ṣafikun antioxidant, oluranlowo ọna asopọ agbelebu ati awọn eroja ẹya miiran, ti ṣelọpọ nipasẹ awọn ohun elo extruding pipade to ti ni ilọsiwaju. O ni ohun-ini extrusion ti o dara julọ ati ohun-ini ti ara, akoonu aimọ rẹ ni iṣakoso laarin awọn opin. Ọja yii ni a lo ni akọkọ bi idabobo ti awọn kebulu ọna asopọ agbelebu alabọde-kekere. Iwọn otutu iṣẹ igba pipẹ jẹ 90 ℃.
Atọka ilana
Ṣeduro lati ṣe ilana pẹlu PE extruder
| Awoṣe | Machine Barrel otutu | Iwọn otutu mimu |
| OW-YJ-10 | 100-115 ℃ | 110-115 ℃ |
Imọ paramita
| Rara. | Nkan | Ẹyọ | Awọn ibeere imọ-ẹrọ | |
| 1 | iwuwo | g/cm³ | 0,922 ± 0,003 | |
| 2 | Agbara fifẹ | MPa | ≥13.5 | |
| 3 | Elongation ni Bireki | % | ≥350 | |
| 4 | Brittle otutu pẹlu Low otutu | ℃ | -76 | |
| 5 | 20 ℃ Iwọn Resistivity | Ω·m | ≥1.0×10¹⁴ | |
| 6 | 20 ℃ Agbara Dielectric, 50Hz | MV/m | ≥25.0 | |
| 7 | 20 ℃ Dielectric Constant, 50Hz | – | ≤2.35 | |
| 8 | 20℃ Dielectric Dissip Factor,50Hz | – | ≤0.001 | |
| 9 | Àkóónú àìmọ́ (Fún 1.0Kg) 0.175-0.250mm ≥0.250 mm | (Rara.) (Rara.) | –– | |
| 10 | Air Ti ogbo Ipò 135 ℃× 168h | Iyatọ Agbara Agbara Lẹhin ti ogbo | % | ≤±20 |
| Elongation Iyatọ Lẹhin ti ogbo | % | ≤±20 | ||
| 11 | Gbona Ṣeto Igbeyewo Ipò 200℃×0.2MPa×15min | Gbona Elongation | % | ≤80 |
| Akiyesi: Awọn alaye diẹ sii, jọwọ kan si oṣiṣẹ tita wa. | ||||
ỌFẸ awọn ofin Ayẹwo
AGBAYE ỌKAN ti ni ifaramọ Lati Pese Awọn alabara Pẹlu Industleading Waya Didara Didara Ati Awọn Ohun elo Cable Ati Awọn iṣẹ Imọ-kikọ akọkọ
O le Beere Apeere Ọfẹ ti Ọja ti o nifẹ ninu eyiti o tumọ si pe o fẹ lati lo ọja wa fun iṣelọpọ
A Nikan Lo Data Experimental Ti O Ṣetan Lati Idahun Ati pinpin Bi Imudaniloju Awọn abuda Ọja Ati Didara, Ati lẹhinna Ran Wa lọwọ Lati Ṣe agbekalẹ Eto Iṣakoso Didara Didara diẹ sii Lati mu Igbekele Awọn alabara ati Ikanra rira, nitorinaa Jọwọ tun ni idaniloju
O le Fọwọsi Fọọmu Lori Ọtun Lati Beere Ayẹwo Ọfẹ
Ohun elo Awọn ilana
1 . Onibara naa ni akọọlẹ Ifijiṣẹ Kariaye Kariaye tabi atinuwa San ẹru naa (Ẹru naa le Pada Ni aṣẹ naa)
2 . Ile-iṣẹ Kanna le Waye Fun Ayẹwo Ọfẹ Kan Ti Ọja Kanna, Ati Ile-iṣẹ Kanna le Waye Fun Titi Awọn Apẹrẹ marun ti Awọn Ọja oriṣiriṣi Fun Ọfẹ Laarin Ọdun kan
3 . Ayẹwo naa jẹ Fun Waya ati Awọn alabara Factory Cable nikan, Ati fun Eniyan ti yàrá nikan fun Idanwo iṣelọpọ tabi Iwadi
Iṣakojọpọ Ayẹwo
Fọọmu ibeere Ayẹwo ỌFẸ
Jọwọ Tẹ Awọn Apejuwe Apeere ti o nilo, tabi Ni ṣoki Ṣapejuwe Awọn ibeere Iṣẹ akanṣe, A yoo ṣeduro Awọn ayẹwo fun Ọ
Lẹhin ifisilẹ fọọmu naa, alaye ti o fọwọsi le jẹ gbigbe si ẹhin AGBAYE ỌKAN fun ilọsiwaju siwaju lati pinnu pato ọja ati alaye adirẹsi pẹlu rẹ. Ati pe o le tun kan si ọ nipasẹ tẹlifoonu. Jọwọ ka waAsiri AfihanFun alaye diẹ sii.